Model NO.
N-PTFE+PPS+FG/FG-900G
Medium Material
Chemical Synthetic Fiber
Dust Collecting Method
Half Dry
Type
Pulse Control
Application
High Temperature
Material
Belnd
Transport Package
Carton+Pallet
Specification
750GSM, DiaxLength
Trademark
HRPuri
Origin
China
HS Code
8451500000
Production Capacity
80000PCS/Month
Certification:
SGS
Installation Method:
Horizontal
Operation Type:
Manually
Material TDS as Follows
Bag top normally has two types of structures, or customised:
| PPS +PTFE Blended Felt PFTE Emulsion Soaking | N-(PTFE+PPS+FG)/FG-900G 30% Super fine PPS fabric on surface |
| Weight per Square Meter (Normal) | 900 G |
| Material (Fiber/Scrim) | (PTFE40%+PPS30%+FG30%)/FG |
| Thickness | 2.8 mm |
| Air permeability | 24 M3/M2.Min@200Pa |
| Warp Tensile Strength | > 2500N/5×20cm |
| Weft Tensile Strength | > 2500N/5×20cm |
| Warp Elongation | < 10%/(5×20cm) |
| Weft Elongation | < 15%/(5×20cm) |
| Continuous service Temperature | < 240ºC |
| Instant (<10Min.) Temperature bears | < 260ºC |
| Liner Shrinkage@130 ºC | MD<0.3%, XD<0.3% |
| Mechanical Finish | Heat Setting, Calendering |
| Chemical Finish | / |
| Mullen (PSI) | / |
| Water Repellent | / |
| Surface Electric-Resistance | / |
| Special Surface or Deep Treatment (In case client specially request to) | PTFE Membrane Laminated (PTFE-ML), or PFTE Emulsion Soaking (PTFE-ES) |
| Other Customise Requests | Acceptable depends on MOQ. |
Bag top normally has two types of structures, or customised: