Introduction:
Ultra-high molecular weight polyethylene(UHMWPE) dock fender could avoid the impact damage between ships and dock. Because of the high impact resistance performance, UHMWPE dock fender instead of the traditional steel ones is widely used in ports and docks at home and abroad.
Our UHMW PE-1000 marine fenders are made from virgin uhmwpe material, which is much superior to wood and rubber in building marine constructions or coastal protective structures. UHMW PE-1000 marine fenders allow vessels to glide easily along the surface, protecting hulls and dock structures. Impervious to marine bore worms with minimum cleaning.
Feature:
1.Highest abrasion resistance of any polymer, 6 times more wear resistance than steel
2.Anti-weather & anti-aging
3.Self-lubricating and very low coefficient of friction
4.Excellent chemical & corrosion resistant; Stable chemical property and can endure the corrosion of all kind of corrosive medium and organic solvent in certain range of temperature and humidity.
5.Superior impact resistant, noise-absorption and vibration-absorption;
Low water absorption <0.01% water absorption and not affected by temperature.
6.Temperature range: -269ºC~+85ºC;
Very high resistance to cold, doesn't become fragile even under -180ºC.
7.High tensile strength
8.Non-toxic and no odor
9.UV resistance and long service life
10.Good performance in resisting environment stress crack
Technical data:
| Property | Unit | Value |
| Density | g/cm3 | 0.93-0.96 |
| Average molecular weight | g/mol | 3million- 10 million |
| Tensile strength (23°C in air) | MPa | 22 |
| Breaking strength | MPa | 42 |
| Tensile strain at break | % | 600 |
| Charpy impact strength (notched) | mJ/mm2 | No break |
| Ball indentation hardness | N/mm2 | 42 |
| Shore hardness | -- | 65-70 |
| Abrasion | % | 70-80, steel = 100 |
| Static Friction Coefficient | -- | ≤0.16 |
| Kinetic Friction Coefficient | -- | ≤0.10 |
| Water Absorption | -- | NIL |
| Elongation at break at 23°C | % | ≥300 |
| Temperature Resistance | °C | -269 to +85 |
| Melt Temperature | °C | 130-140 |
Application:
1.Harbour instruction :
Wear pad to replace wood and rubber
protective quay wall
2.truck dock
fenders for dock plate protection
3.Piling
Fenders
Wear plate and slides
4.floating dock
wear plate where dock meets pillage
fenders
Slides
Key words:
UHMW-PE wear plastic plate polyethylene dock fender panel / high impact uhmwpe marine fender pad
Send Message