LATP solid state battery electrolyte has received extensive attention because of its excellent chemical and thermodynamic stability, extremely low raw material cost and preparation cost. It is a nano-solid electrolyte material that can be used for the preparation of all-solid-state lithium-ion batteries.
Model: TOB-LATP-E01
Conductivity: 2*10-4S/cm
Optional specifications:
1. Square 60*60mm
2. Single piece packaging with diameter of 12mm*260μm
3. Other sizes can be customized
Product name | Lithium Aluminum Titanium Phosphate Solid State Battery Electrolyte Sheet | ||
Specification | Round sheet, diameter 12mm, thickness 260μm | ||
Theoretical density | 2.94g/cm3 | ||
Chemical formula | Li1.3Al0.3Ti1.7P3O12 | ||
Shelf life | 1 year | ||
| |||
Items | Qualification standards | Unit | Detection method |
Thickness | 260±10 | μm | Micrometer |
Diameter | 12±0.1 | mm | Vernier caliper |
Appearance | White, uniform color | / | Visual inspection |
Main crystal phase | Consistent with the characteristic peak of PDF#35-0754 | / | XRD |
Ceramic sample ion conductivity@25ºC | ≥0.45 | mS/cm | AC impedance method |
Flexural strength | ≥130 | MPa | Three-point bending resistance |
Density | ≥2.793 | g/cm3 | Drainage method |
Densification | ≥95 | % | Density/theoretical density*100% |
Micromorphology | Magnification 20000, no more than 3 holes | / | SEM |